"We produce homopolymer, random copolymer, and impact copolymer polypropylene resins for a wide range of use, marketed under the Trilene brand name"
We produce homopolymer, random copolymer, and impact copolymer polypropylene resins for a wide range of use, marketed under the Trilene brand name. Applications include the various film, yarn, and multi-filament extrusion processes, injection molding, blow molding, and thermoforming.
Consisting only of propylene molecules. Have high tensile strength, stiffness, heat resistance, and hardness properties. These "homopolymer" suitable for broad range applications such as Films, Injection Molding, Sheet thermoforming, Yarn, and Fiber Multifilament.
Consisting only of propylene molecules. Have high tensile strength, stiffness, heat resistance, and hardness properties. These "homopolymer" suitable for broad range applications such as Films, Injection Molding, Sheet thermoforming, Yarn, and Fiber Multifilament.
To benefit from some of the useful properties of ethylene, about 1 - 7% by weight of ethylene monomer is added into the propylene monomer simultaneously in the reactor. The inclusion of the ethylene molecule reduces the polypropylene's crystalinity producing improved transparency and better strength compared with homopolymers.
To benefit from some of the useful properties of ethylene, about 1 - 7% by weight of ethylene monomer is added into the propylene monomer simultaneously in the reactor. The inclusion of the ethylene molecule reduces the polypropylene's crystalinity producing improved transparency and better strength compared with homopolymers.
With the insertion of an ethylene/propylene rubber phase coating at the surface of the semi crystalline homopolymer matrix, the impact copolymer offers improved impact strength compared to the homopolymer or the random copolymer injection grade, at the cost of stiffness.
With the insertion of an ethylene/propylene rubber phase coating at the surface of the semi crystalline homopolymer matrix, the impact copolymer offers improved impact strength compared to the homopolymer or the random copolymer injection grade, at the cost of stiffness.