PT. Tri Polyta Indonesia Tbk.

Trilene HE2.0TF is a polypropylene homopolymer for sheet extrusion and thermoforming (SPPF) applications. This grade uses Unipol^® polypropylene technology.

Good clarity
Good impact strength
Excellent stiffness
Excellent processability
Compliance with FDA regulation 21CFR177.1520

PRODUCT DATA SHEET

Physical Properties

SI Units

ASTM Test*

Metric Units

Melt Flow Rate (MFR)
(230°C/2.16 kg)

2.4 g/10 min

D1238

2.4 g/10 min

Density

903 kg/m³

D792

0.903 g/cm³

Tensile yield strength
at 50 mm/min

36 MPa

D638

367 kg/cm²

Tensile yield elongation

14%

D638

14%

Flexural modulus (1% secant)
at 1.3 mm/min

1290 MPa

D790A

13158 kg/cm²

Notched Izod impact strength
at 23°C

44 J/m

D256

4.5 kg-cm/cm

Hardness, Rockwell

R94

D785

R94

Deflection temperature
at 0.455 MPa (4.64 kg/cm²)

104°C

D648

104°C

Vicat softening temperature

152°C

D1525B

152°C

Melting temperature
DSC, 10 C/min, 2^nd heat

161°C

D3418

161°C

Processing temperature	:	Melt temperature	220-240°C
		Chill roll temperature	25-40°C
		Sheet temp. at forming zone	157-160°C

* Polypropylene tested per ASTM D4101.