PT. Tri Polyta Indonesia Tbk.

RI10HO is a polypropylene ethylene random copolymer with good clarity, for housewares, containers, closures, plastic hanger, and general purpose injection molding applications. Where good impact properties is desired. This grade uses Unipol^® polypropylene technology Union Carbide Corporation with the latest generation of catalyst.

Good clarity & good flexibility
Better impact strength than homopolymer
Compliance with FDA regulation 21CFR177.1520

PRODUCT DATA SHEET

Physical Properties

SI Units

ASTM Test*

Metric Units

Melt Flow Rate (MFR)
(230°C/2.16 kg)

10 g/10 min

D1238

10 g/10 min

Density

895 kg/m³

D792

0.895 g/cm³

Tensile yield strength
at 50 mm/min

27 MPa

D638

276 kg/cm²

Tensile yield elongation

15%

D638

15%

Flexural modulus (1% secant)
at 1.3 mm/min

1000 MPa

D790A

10200 kg/cm²

Notched Izod impact strength
at 23°C

88 J/m

D256

8.9 kg-cm/cm

Hardness, Rockwell

R81

D785

R81

Deflection temperature
at 0.455 MPa (4.64 kg/cm²)

85°C

D648

85°C

Vicat softening temperature

125°C

D1525B

125°C

Melting temperature
DSC, 10 C/min, 2^nd heat

146°C

D3418

146°C

Processing temperature	:	Injection temperature		230-240°C
		Mold temperature		20-40°C

* Polypropylene tested per ASTM D4101.