Trilene BI9.0GA is an Impact Copolymer Polypropylene (ICP) for housewares, pail for paint Automotive parts, electric appliance part that requiring good impact strength. This grade use Unipol^® polypropylene technology.

High impact strength and stiffness balance
Easy to process
Good drop test
Compliance with FDA regulation 21CFR177.1520

PRODUCT DATA SHEET

Physical Properties

SI Units

ASTM Test*

Metric Units

Melt Flow Rate (MFR)
(230°C/2.16 kg)

9.0 g/10 min

D1238

9.0 g/10 min

Density

900 kg/m³

D792

0.900 g/cm³

Tensile yield strength
at 50 mm/min

28 MPa

D638

285 kg/cm²

Tensile yield elongation

12%

D638

12%

Flexural modulus (1% secant)
at 1.3 mm/min

1230 MPa

D790A

12500 kg/cm²

Notched Izod impact strength
at 23°C

140 J/m

D256

14 kg-cm/cm

Hardness, Rockwell

R80

D785

R80

Deflection temperature
at 0.455 MPa (4.64 kg/cm²)

100°C

D648

100°C

Vicat softening temperature

148°C

D1525B

148°C

Melting temperature
DSC, 10 C/min, 2^nd heat

163°C

D3418

163°C

Processing temperature	:	Injection temperature		220-240°C
		Mold temperature		20-40°C

* Polypropylene tested per ASTM D4101.