Trilene BI32AN is a nucleated Impact Copolymer Polypropylene (ICP) for electronic appliances, automotive and general purpose applications requiring high flow and impact strength. This grade is nucleated to provide lower warpage, greater modulus, and faster cycle time. This grade uses Unipol^® polypropylene technology.

Excellent processability with faster cycle time
High stiffness
Reduced warpage
Good impact strength
Compliance with FDA regulation 21CFR177.1520

PRODUCT DATA SHEET

Physical Properties

SI Units

ASTM Test*

Metric Units

Melt Flow Rate (MFR)
(230°C/2.16 kg)

32 g/10 min

D1238

32 g/10 min

Density

900 kg/m³

D792

0.900 g/cm³

Tensile yield strength
at 50 mm/min

29 MPa

D638

295 kg/cm²

Tensile yield elongation

11%

D638

11%

Flexural modulus (1% secant)
at 1.3 mm/min

1300 MPa

D790A

13300 kg/cm²

Notched Izod impact strength
at 23°C

100 J/m

D256

10 kg-cm/cm

Hardness, Rockwell

R85

D785

R85

Deflection temperature
at 0.455 MPa (4.64 kg/cm²)

105°C

D648

105°C

Vicat softening temperature

148°C

D1525B

148°C

Melting temperature
DSC, 10 C/min, 2^nd heat

163°C

D3418

163°C

Processing temperature	:	Injection temperature		200-240°C
		Mold temperature		20-50°C

* Polypropylene tested per ASTM D4101.