PT. Tri Polyta Indonesia Tbk.

Trilene HS35NW is an extra high flow polypropylene homopolymer for spundbond non-wovens The end applications include apparel covers, shoping bags, napkins and disposal cloth. This grade uses Unipol^®polypropylene technology.

Excellent flow and suitable for fine denier spunbond non-wovens
Narrow molecular weight distribution
Excellent drawability and spinnability process
Contained antistatic agent and low ethylene random
Compliance with FDA regulation 21CFR177.1520

PRODUCT DATA SHEET

Physical Properties

SI Units

ASTM Test*

Metric Units

Melt Flow Rate (MFR)
(230°C/2.16 kg)

35 g/10 min

D1238

35 g/10 min

Density

903 kg/m³

D792

0.903 g/cm³

Tensile yield strength
at 50 mm/min

33 MPa

D638

336 kg/cm²

Tensile yield elongation

13%

D638

13%

Flexural modulus (1% secant)
at 1.3 mm/min

1260 MPa

D790A

12850 kg/cm²

Notched Izod impact strength
at 23°C

30 J/m

D256

3.1 kg-cm/cm

Hardness, Rockwell

R100

D785

R100

Deflection temperature
at 0.455 MPa (4.64 kg/cm²)

104°C

D648

104°C

Vicat softening temperature

152°C

D1525B

152°C

Melting temperature
DSC, 10 C/min, 2^nd heat

163°C

D3418

163°C

Processing temperature	:	Melt temperature		200-240°C
		Cooling temperature		20-25°C

* Polypropylene tested per ASTM D4101.