PT. Tri Polyta Indonesia Tbk.

Trilene HF8.0CM is a polypropylene homopolymer for production of cast film, including film to be metallized. This grade uses Unipol^® polypropylene technology with the latest catalyst technology.

High strength
Excellent clarity
Good processability
Compliance with FDA regulation 21CFR177.1520

PRODUCT DATA SHEET

Physical Properties

SI Units

ASTM Test*

Metric Units

Melt Flow Rate (MFR)
(230°C/2.16 kg)

8.0 g/10 min

D1238

8.0 g/10 min

Density

903 kg/m³

D792

0.903 g/cm³

Tensile yield strength
at 50 mm/min

35 MPa

D638

357 kg/cm²

Tensile yield elongation

13%

D638

13%

Flexural modulus (1% secant)
at 1.3 mm/min

1280 MPa

D790A

13050 kg/cm²

Notched Izod impact strength
at 23°C

30 J/m

D256

3.1 kg-cm/cm

Hardness, Rockwell

R102

D785

R102

Deflection temperature
at 0.455 MPa (4.64 kg/cm²)

104°C

D648

104°C

Vicat softening temperature

152°C

D1525B

152°C

Melting temperature
DSC, 10 C/min, 2^nd heat

163°C

D3418

163°C

Processing temperature	:	Extrusion temperature		240-260°C
		Chill roll temperature		30°C

* Polypropylene tested per ASTM D4101.