PT. Tri Polyta Indonesia Tbk.

Trilene HY3.8FY is a polypropylene homopolymer for production of stretched tape (yarn or raffia). Also can be use for for transparent woven bag which require good clarity, stiffness. This grade uses Unipol^® polypropylene technology.

Excellent processability, cosistent denier

Excellent strength, tenacity and % elongation balance

Good clarity and transparancy for laminated rice bag

Low water carryover

Compliance with FDA regulation 21CFR177.1520

PRODUCT DATA SHEET

Physical Properties

SI Units

ASTM Test*

Metric Units

Melt Flow Rate (MFR)
(230°C/2.16 kg)

3.8 g/10 min

D1238

3.8 g/10 min

Density

903 kg/m³

D792

0.903 g/cm³

Tensile yield strength
at 50 mm/min

34 MPa

D638

347 kg/cm²

Tensile yield elongation

13%

D638

13%

Flexural modulus (1% secant)
at 1.3 mm/min

1290 MPa

D790A

13150 kg/cm²

Notched Izod impact strength
at 23°C

40 J/m

D256

4.1 kg-cm/cm

Hardness, Rockwell

R100

D785

R100

Deflection temperature
at 0.455 MPa (4.64 kg/cm²)

104°C

D648

104°C

Vicat softening temperature

152°C

D1525B

152°C

Melting temperature
DSC, 10 C/min, 2^nd heat

163°C

D3418

163°C

Processing temperature	:	Melt temperature		230-250°C
		Water bath temperature		27-35°C

* Polypropylene tested per ASTM D4101.