Melt Flow Rate (MFR)
(230°C/2.16 kg) |
|
10 g/10 min
|
|
D1238
|
|
10 g/10 min
|
|
| |
Tensile yield strength
at 50 mm/min |
|
34 MPa
|
|
D638
|
|
346 kg/cm²
|
|
| |
Flexural modulus (1% secant)
at 1.3 mm/min |
|
1280 MPa
|
|
D790A
|
|
13050 kg/cm²
|
|
| |
Notched Izod impact strength
at 23°C |
|
35 J/m
|
|
D256
|
|
3.6 kg-cm/cm
|
|
| |
Deflection temperature
at 0.455 MPa (4.64 kg/cm²) |
|
104°C
|
|
D648
|
|
104°C
|
|
| |
Vicat softening temperature |
|
152°C
|
|
D1525B
|
|
152°C
|
|
| |
Melting temperature
DSC, 10 C/min, 2nd heat |
|
163°C
|
|
D3418
|
|
163°C
|
|
| |
| Processing temperature |
:
|
Injection temperature |
|
220-250°C
|
|
|
Molt temperature |
|
20-40°C
|
|
|
|
* Polypropylene tested per ASTM D4101.
|